Jis H 8625 Pdf Online
If you are specifying anodized aluminum for building facades, curtain walls, or windows, this PDF document is arguably more critical than any other single reference. Unlike decorative anodizing standards, JIS H 8625 is exclusively for architectural exteriors . The standard acknowledges that buildings face acid rain, coastal salt, UV radiation, and alkaline cement runoff.
⚠️ 9 µm (Class I) is roughly 0.35 mils. Compare to AAMA 611 which requires 10 µm (0.4 mils) or 18 µm for coastal. Some engineers argue JIS Class I is insufficient for aggressive beachfront buildings. jis h 8625 pdf
JIS H 8625 is an excellent, demanding, and well-structured standard for architectural anodizing. Its reliance on CASS testing and quantitative admittance sets it apart from softer international standards. However, it is not the heaviest-duty standard (AAMA is tougher for coastal US), and its low thickness limit (9 µm) requires the specifier to add a note for aggressive environments. If you are specifying anodized aluminum for building
The standard introduces the CASS Test (Copper Accelerated Acetic Acid Salt Spray) as mandatory for top-tier finishes. This is brutal. Many Western standards only require neutral salt spray (NSS). JIS H 8625 demands copper-accelerated testing to simulate severe marine/industrial environments. 3. The Critical Classification System | Feature | Class I (Superior) | Class II (General) | | :--- | :--- | :--- | | Min. Thickness | ≥ 9 µm (often spec’d higher) | ≥ 7 µm | | Sealing Quality | Excellent (Low admittance) | Good | | CASS Test (8 hrs) | No corrosion pits after 8h | Pits allowed but limited | | Application | Coastal areas, high pollution, curtain walls | Inland, mild environments, window frames | ⚠️ 9 µm (Class I) is roughly 0